MIG ALUMINIUM WELDING WIRE ER4047 FOR PACKING IN METAL SPOOL

MIG ALUMINIUM WELDING WIRE ER4047 FOR PACKING IN METAL SPOOL,OEM,Metallurgy, Chemicals,Minerals & Metallurgy,Aluminum,Aluminum Wire

INQUIRY PRECISE INQUIRY

Description

Overview

Quick Details

Place of Origin:: Shandong, China (Mainland)

Surface Treatment:: Color Coated

Alloy Or Not:: Is Alloy

Al (Min):: <0.10

Ultimate Strength (≥ MPa):: 25 Mpa

Elongation (≥ %):: 18%

Conductivity:: yes

Brand Name:: OEM

Model Number:: ER4047

Application:: bicycles, aluminium scoter

Wire Gauge:: 1.6mm

Standard:: GB/T23309-2009 Aluminium Wire

Certificate:: ISO9001:2008

Type:: MIG

Material:: 14 Gauge Aluminum Alloy Wire

Feature:: Bright Color

Diameter:: 1.6/2.0/2.4/3.2/4.0/4.8mm

Packing:: Wooden Pallet

Shape:: Strip

Purity:: 95% 99.7%

Packaging & Delivery

Selling Units:: Single item

Single package size:: 30.5X30.5X10.6 cm

Single gross weight:: 7.7 KG

Package Type:: 7kg/spool 1 spool in 1 carton 72 carton in 1 pallet

Lead Time :

Quantity(Kilogram)	1 - 5000	>5000
Est. Time(day)	10	To be negotiated

MIG ALUMINIUM WELDING WIRE ER4047 FOR PACKING IN METAL SPOOL

Aluminum welding wire is specialized in production pure aluminum welding rod, aluminum magnesium welding rod, aluminum silicon welding rod, low silicon welding rod, high silicon welding rod.The aluminum welding wires are widely used in bicycles, aluminium scoter, engine carriage, pressure vessel, armary processing, ship-building, space shuttle etc.

AWS A 5-10 Data		ER1060	ER1100	ER2319	ER4043	ER4047	ER5356	ER5183	ER5556
Typical composition in%	Si	<0.25	Si+Fe<0.95	<0.20	4.50-5.50	11.00-13.00	<0.25	<0.40	<0.25
	Fe	<0.35	Si+Fe<0.95	<0.30	<0.80	<0.60	<0.40	<0.40	<0.40
	Cu	<0.05	0.05-0.20	5.80-6.80	<0.30	<0.30	<0.10	<0.10	<0.10
	Mn	<0.03	<0.05	0.20-0.40	<0.05	<0.15	0.05-0.20	0.50-1.00	0.60-1.00
	Mg	<0.03	-	<0.02	<0.05	<0.10	4.50-5.50	4.30-5.20	4.70-5.50
	Cr	-	-				0.05-0.20	0.05-0.25	0.05-0.20
	Zn	<0.05	<0.10	<0.10	<0.10	<0.20	<0.10	<0.25	<0.20
	Be	-	<0.0008	<0.0003	<0.0003	<0.0003	<0.0003	<0.0003	<0.0003
	Ti	<0.03	-	0.10-0.20	<0.20	<0.15	0.06-0.20	<0.15	0.05-0.20
Physical properties(Approx. Values)	0.2% yield strength Rp0.2 Mpa	20	25	180	40	60	110	125	125
	Tensile strength Rm Mpa	65	80	240	120	130	240	275	275
	Elongation A5(L0=5d0) %	18	25	Ca.3	8	5	17	17	17
	Test temperature ℃	20	20	20	20	20	20	20	20

AWS A5.10	Joint Strength	Parent metal	Characteristics
Standard	(Mpa)	Parent metal	Characteristics
ER1070	Above 55	Pure aluminum series105010701080	Good anti-corrosive and plasticity
ER1100	80-110	Pure aluminum series1100	Good anti-corrosive and plasticity
ER1200	80-110	Pure aluminum series1200	Good anti-corrosive and plasticity
ER2319	400-450	Pure aluminum series2219	High intensity after heat treatment
ER4043	170-250	Al-Mg-Si casting aluminum	The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER4047	170-250	Casting Al. ,Al-Cu casting ,Ag-Mg-Si casting	The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER4145	200-300	Al-Cucasting20142017	The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER5554	180-240	low Mg content5052,5454casting	Use chemical equipment with a temperature above 65
ER5654	210-270	medium Mg content5154casting	medium intensity,good anti-corrosive
ER5356	270-310	Al-Mg casting, Al-Mg-Si casting, Al-Zn-Mg casting	Typical welding wire used most widely, good mechanics performance and anti-corrosiveness
ER5556	280-320	Al-Zn-Mg casting, Al-Mg casting	The connector intensity is high, and the moulding performance and tenacity is inferior to 5183
ER5183	280-310	Al-Mgcasting5083	Typical welding wire used most widely, good mechanical performance and anti-corrosiveness